The Department of Applied Physics of The Hong Kong Polytechnic University (PolyU) has developed a simple approach to synthesize novel environmentally-friendly manganese dioxide (MnO2) ink by using glucose. The MnO2 ink could be used for the production of light, thin, flexible and high performance energy storage devices via ordinary printing or even home-used printers.
The capacity of the MnO2 ink supercapacitor is more than 30 times higher than that of a commercial capacitor of the same weight of active material (e.g. carbon powder), demonstrating the great potential of MnO2 ink in significantly enhancing the performances of energy storage devices, whereas its production cost amounts to less than HK$1.
MnO2 is a kind of environmentally-friendly material and it is degradable. Given the environmental compatibility and high potential capacity of MnO2, it has always been regarded as an ideal candidate for the electrode materials of energy storage devices. The conventional MnO2electrode preparation methods suffer from high cost, complicated processes and could result in agglomeration of the MnO2 ink during the coating process, leading to the reduction of electrical conductivity.
The PolyU research team has developed a simple approach to synthesize aqueous MnO2 ink. Firstly, highly crystalline carbon particles were prepared by microwave hydrothermal method, followed by a morphology transmission mechanism at room temperature. The MnO2 ink can be coated on various substrates, such as conductive paper, plastic and glass. Its thickness and weight can also be controlled for the production of light, thin, transparent and flexible energy storage devices. Substrates coated by MnO2 ink can easily be erased if required, facilitating the fabrication of electronic devices.
PolyU researchers coated the MnO2 ink on conductive A4 paper and fabricated a capacitive energy storage device with maximum energy density and power density amounting to 4 mWh•cm-3 and 13 W•cm-3 respectively. The capacity of the MnO2 ink capacitor is more than 30 times higher than that of a commercial capacitor of the same weight of active material (e.g. carbon powder), demonstrating the great potential of MnO2 ink in significantly enhancing the performances of energy storage devices. Given the small size, light, thin, flexible and high energy capacity properties of the MnO2 ink energy storage device, it shows a potential in wide applications.
For instance, in wearable devices and radio-frequency identification systems, the MnO2 ink supercapacitor could be used as the power sources for the flexible and “bendable” display panels, smart textile, smart checkout tags, sensors, luggage tracking tags, etc., thereby contributing to the further development of these two areas.
The Latest on: MnO2 ink supercapacitor
via Google News
The Latest on: MnO2 ink supercapacitor
- Capacitors Are Simple, Right?on December 6, 2019 at 4:00 pm
If you want to read more about capacitors, you might enjoy our recent coverage of capacitor types. If supercapacitors strike your fancy, you can always grab some lint and dog hair.
- Journal of nanoscience and nanotechnologyon December 1, 2019 at 4:00 pm
Fabrication of Sn-3.5Ag Eutectic Alloy Powder by Annealing Sub-Micrometer [email protected] Powder Prepared by Citric Acid-Assisted Ag Immersion Plating. High Quality Al-Polar AIN Growth on (0001) Sapphire Using ...
- Non-toxic printed supercapacitors operating in sub-zero conditionson October 1, 2019 at 2:10 am
Aqueous supercapacitors offer a safe alternative for intermediate ... First, the current collector was printed with Henkel Electrodag PF407C graphite ink and cured at 120 °C for 15 min in a forced ...
- Nano4Energy - clean, next generation energy solutionson September 19, 2019 at 5:00 pm
At the University of Surrey, Birnessite MnO2 nanotubes have been made and cast into self - supporting electrode films. Supercapacitor cells were assembled ... quantum dots capable of forming printable ...
- Manganese oxide synthesized from spent Zn-C battery for supercapacitor electrode applicationon June 19, 2019 at 5:00 pm
XRD diffraction peaks of spent battery powder shown in Fig. 1b confirmed the presence of mainly ZnMn 2 O 4 (hetaerolite) and Zn 5 (OH) 8 Cl 2 H 2 O (simonkolleite) phases which formed due to the ...
- 3D Printed Graphene Aerogel May Lead to Powerful Supercapacitorson October 23, 2018 at 1:55 am
In a study entitled “Efficient 3D Printed Pseudocapacitive Electrodes with Ultrahigh MnO2 Loading,” a group of researchers at UC Santa Cruz and Lawrence Livermore National Laboratory have achieved ...
- 3D-printed supercapacitor electrode breaks records in lab testson October 18, 2018 at 12:11 pm
The printable graphene-based inks developed at LLNL provide ultrahigh surface area, lightweight properties, elasticity, and superior electrical conductivity. University of California - Santa Cruz.
- PolyU develops novel eco high performance energy storage deviceon September 23, 2015 at 6:49 am
The capacity of the MnO2 ink supercapacitor is more than 30 times higher than that of a commercial capacitor of the same weight of active material (e.g. carbon powder), demonstrating the great ...
- Team develops novel eco high performance energy storage deviceon September 22, 2015 at 5:00 pm
flexible and high performance energy storage devices via ordinary printing or even home-used printers. The capacity of the MnO2 ink supercapacitor is more than 30 times higher than that of a ...
- Graphene ready for commercialisationon March 28, 2012 at 5:09 pm
Graphene is ready for commercialisation ... Zhang proposed graphene-oxide e.g ZnO, SnO2, Co3O4, MnO2, or graphene-polymer, or graphene-CNT for supercapacitors, and Li-Ion batteries; graphene-TiO2 for ...
via Bing News